第五章 生醫陶瓷(Bioceramics)

生醫陶瓷根據其與動物組織間的反應程度,可分為三大類:[1,2]  

1.    可吸收性生醫陶瓷(Completely Resorbable Bioceramics):

    置於人體後,會逐漸溶解而被其周圍組織而取代。這一類陶瓷有三鈣磷酸鹽(Ca3((PO)4)2,TCP)、非晶質磷酸鹽(amorphous calcium phosphates,ACP)、貧鈣磷酸鹽(Calcium deficient apatites,CDA);在體內的吸收速率為ACP>TCP>CDA。[3]

2.    近惰性生醫陶瓷(Nearly Inert Bioceramics):

    置於體液中非常穩定,幾乎不會釋出離子或與組織產生反應,又分為非孔隙性與孔隙性陶瓷;氧化鋁、氧化鋯為其代表。

3.表面活性生醫陶瓷(Surface-Active Bioceramics):

    置於體液中會和組織形成化學鍵結。這一類的陶瓷材料有氫氧基磷灰石、生醫玻璃等材料。

     本章節將分四部分來講:(1) 可吸收性生醫陶瓷,(2) 近惰性生醫陶瓷,(3) 表面活性生醫陶瓷,(4)複合材料

 

參考文獻

1. L. L. Hench and E. C. Ethridge, Biomaterial A cademic Press. Inc. (1982)

2. 洪敏雄,林峰輝,王盈錦,生醫陶瓷 陶瓷技術手冊(下) 中華民國產業科技發展協進會 (1994)

3. G. Daculsi, Biotechnology for Calcium Phosphate Bioactive Ceramics in Bone Repair The Chinese Society for Materials, 1999 Annual Meeting Workshop(1999)

4. S. Saite, T. Oshiuo, T. Saite, Biomaterials, V.19, p.1895-1900 (1998)

5. J. B. Park, Biomaterials Science and Engineering Plennm Inc. (1990)

6. 黃啟祥,林江財,氧化鋁 陶瓷技術手冊(下) 中華民國產業科技發展協進會 (1994)

7. M. Salzer, K. Zweymuller, H. Lake, A. Zeibig, N. Staerk, H. Jr. Penk and G. Punzet, J. Biomed. Biomater. Res., V.10, p.847-856 (1976)

8. A. Chanda, Ceram. Internat., V. 23, p.437-447 (1997)

9. 杜正恭氧化鋯 陶瓷技術手冊(下) 中華民國產業科技發展協進會 (1994)

10.      J. S. Reed, Principles of Ceramics Processing, John Wiley & Sons Inc. (1995)

11.      X. Nie, A. Leyland and A. Matthews, Surf. Coat. Technol. V.125, p.407-414 (2000)

12.      J. M. Gomez-Vega, E. Saiz, A. P. Tomsia, G. W. Marshall and, S. J. Marshall, Biomaterials, V. 21, p.105-111 (2000)

13.      S. K. Yen, Mater. Chem. Phys., V.63 p.256-262 (2000)

14.      F. H. Lin, C. H. Yao, C. W. Huang, H. C. Liu, J. S. Sun and C. Y. Wang, Mater. Chem. Phys., V.46, p.36-42 (1996)

15.      A. J. Salinas, J. Roman, M. Vallet-Regi, J. M. Oliveria, R. N. Correia and M. H. Fernandes, Biomaterials, V. 21, p.251-257 (2000)

16.      S. K. Yen and T. Y. Huang, "Characterization of The Electrolytic ZrO2 Coating on Ti-6Al-4V", Material Chemistry and Physics, Vol. 6, p.214-221 (1998)                     

17.      H. C. Hsu and S. K. Yen,"Evaluation of Metal Ion Release and Corrosion Resistance of ZrO2 Thin Coating on the Dental Co-Cr-Mo Alloys" Dental Materials,Vol.14, p.339-346 (1998)

18.      S. K. Yen, Characterization Electrolytic ZrO2 Coating on AISI 316L Stainless Steel, J. Electrochem. Soc., Vol. 146, No. 4, p. 1392-1397 (1999)

19.      K. A. Khor, Z. L.Dong, C. H. Quek and P. Cheang, Mater. Sci. Engineer. V. A281, p.221-228 (2000)

20.      A. Oliva, A. Salerno, B. Locardi, V. Riccio, F. D. Ragione, P. Iardino and V. Zappia, Biomaterials, V. 91, p.1019-1025 (1998)

21.      許碩文, 電解沉積氧化鋁於鈷鉻鉬合金之研究, 國立中興大學材料工程學研究所八十八學年度碩士論文 (1999)

22.      賴志育, 電解沉積ATZs與ZTAs陶瓷薄膜於鈷鉻鉬合金之研究, 國立中興大學材料工程學研究所八十九學年度碩士論文 (2000)

23.      林奇民, 電解沉積Al2O3-HA陶瓷於純鈦金屬之研究, 國立中興大學材料工程學研究所八十九學年度碩士論文 (2000)

回上一頁